1. n. []

A type of corrosion produced when a metal absorbs hydrogen atoms. This phenomenon can cause undesirable effects such as blistering, cracking, methane formation above 400 degF [204 degC], and hydrogen embrittlement.

See related terms: corrosion control,  hydrogen blistering,  hydrogen embrittlement,  sulfide stress cracking